Tribological Analysis of Copper-Coated Graphite Particle-Reinforced A359 Al/5 wt.% SiC Composites

勤益科大機構典藏 > 工程學院 > 機械工程系(所) > 【機械工程系】期刊論文 > Item 987654321/5786

請使用永久網址來引用或連結此文件: http://ir.lib.ncut.edu.tw/handle/987654321/5786

題名:	Tribological Analysis of Copper-Coated Graphite Particle-Reinforced A359 Al/5 wt.% SiC Composites
作者:	Chu, C. B. LinEmail authorT. C. WangZ. C. ChangH. Y.
貢獻者:	圖書館
關鍵詞:	aluminum matrix composites graphite silicon carbide wear
日期:	2013
上傳時間:	2016-10-13 13:22:12 (UTC+8)
摘要:	Copper-coated graphite particles can be mass-produced by the cementation electroless copper and 5 wt.% SiC particulates were introduced into an aluminum alloy by compocasting to make A359 Al/5 wt.% SiC(p) composite that contained 2, 4, 6, and 8 wt.% graphite particulate composite. The effects of SiC particles, quantity of graphite particles, normal loading, sliding speed and wear debris on the coefficient of friction, and the wear rate were investigated. The results thus obtained indicate that the wear properties were improved by adding small amounts of SiC and graphite particles into the A359 Al alloy. The coefficient of friction of the A359 Al/5 wt.% SiC(p) composite that contained 6.0 wt.% graphite particulates was reduced to 0.246 and the amount of graphite film that was released on the worn surface increased with the graphite particulate content. The coefficient of friction and the wear rate were insensitive to the variationprocess using simple equipment. Graphite particulates that were coated with in the sliding speed and normal loading.
關聯:	Journal of Materials Engineering and Performance
顯示於類別:	[機械工程系(所)] 【機械工程系】期刊論文