Characteristics of Fe-Si-B-Cr-C Powders Synthesized by the Spinning Water Atomization Process (SWAP) and Its Application in Magnetic Core

勤益科大機構典藏 > 工程學院 > 機械工程系(所) > 【機械工程系】期刊論文 > Item 987654321/5817

請使用永久網址來引用或連結此文件: http://ir.lib.ncut.edu.tw/handle/987654321/5817

題名:	Characteristics of Fe-Si-B-Cr-C Powders Synthesized by the Spinning Water Atomization Process (SWAP) and Its Application in Magnetic Core
作者:	Shih Fan Chen, Shih Hang Huang, Shea Jue Wang, Jin Shyong Lin , Shih Hsun Chen, Chien Chon Chen
貢獻者:	圖書館
關鍵詞:	Amorphous Ribbons Powders SWAP
日期:	2015-04
上傳時間:	2016-10-14 09:16:04 (UTC+8)
摘要:	The application properties of magnetic cores made of Fe72.8Si11.2B10.8Cr2.3C2.9 powders was studied. The amorphous Fe72.8Si11.2B10.8Cr2.3C2.9 powders were prepared by a spinning water atomization process (SWAP), and the cores further were fabricated from those powders by a hydraulicpressing process. The particle size distribution of powders was about 10 to 20 μmand the alloy powders would crystallize during milling. For the cores, the maximum permeability μi was 14 and quality factor Q was 84 between 100kHz - 2000kHz for 1 wt.% Na2SiO4solidified with H-epoxy at 300°C. The minimum coercivityHcwas 0.22 Oe at 1 wt.% Na2SiO4 with PVB consolidated at 150 °C, and the maximum saturation magnetization Bm was 7.64×102 G for 2 wt.% Na2SiO4 with H-epoxy at 300 °C.