Scratch Characteristics of ZnMgO Epilayers

勤益科大機構典藏 > 工程學院 > 機械工程系(所) > 【機械工程系】期刊論文 > Item 987654321/5822

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncut.edu.tw/handle/987654321/5822

题名:	Scratch Characteristics of ZnMgO Epilayers
作者:	Hua-Chiang Wen, Wu-Ching Chou,Tun-Yuan Chiang,Wen-Chung Fan,Ling Lee
贡献者:	圖書館
关键词:	Metal organic vapor phase epitaxy Friction Nanoscratch
日期:	2015-03-22
上传时间:	2016-10-14 09:35:04 (UTC+8)
摘要:	Zn0.75Mg0.25O films were grown via metal organic vapor phase epitaxy on an M-plane sapphire substrate. We used nanoscratch tests to study the abrasive plow of the films; comparable cases of critical pileup were obtained on both sides of each scratch when the ramped load increased from 0 to 250 μN. The film showed a crack in the bulge edge between the groove at ramped loads of 1000 μN as well as full plastic deformation. The values of μ were 0.14, 0.33, 0.43, and 0.48 for the ramped loads of 250 μN and 0.22, 0.26, 0.28, and 0.33 for the ramped load of 1000 μN. We found that cracking dominated in the case of Zn0.75Mg0.25O films during plowing. Lower values of the coefficient of friction and shallower penetration depths were observed at RT, while higher values were observed in the annealed samples. It is suggested that higher growth temperatures induce lower bonding forces and reduce the shear resistances of Zn0.75Mg0.25O films.
關聯:	Tribology Letters
显示于类别:	[機械工程系(所)] 【機械工程系】期刊論文