Characterization of cobalt monoxide thin film modified with silicon dioxide prepared by the cathodic deposition for lithium-ion battery

勤益科大機構典藏 > 工程學院 > 化工與材料工程系(所) > 【化工與材料工程系】期刊論文 > Item 987654321/5836

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncut.edu.tw/handle/987654321/5836

题名:	Characterization of cobalt monoxide thin film modified with silicon dioxide prepared by the cathodic deposition for lithium-ion battery
作者:	Jing-Shan Do, Wei-Han Ko, Rui-Feng Dai
贡献者:	圖書館
关键词:	Cobalt monoxide Silicon dioxide Tetraethyl orthosilicate Anode Lithium battery
日期:	2015-06
上传时间:	2016-10-14 11:34:24 (UTC+8)
摘要:	The precursor (cobalt hydroxide, Co(OH)2) of cobalt oxide (CoO) is cathodically electrodeposited on copper foil in cobalt nitrate and sodium nitrated aqueous solution. CoO can be obtained by calcinating Co(OH)2 for the temperature greater than 500 °C in N2 atmosphere. For the preparation of Co(OH)2 in the presence of silicon rubber as the sealant to define the electrodepositing area, some co-deposited components dissolved from silicon rubber are converted to SiO2 in the calcination process. The charge/discharge performances of CoO thin film are enhanced by the presence of SiO2. When the TEOS (tetraethyl orthosilicate) is added into the solution for electrodepositing the precursor of CoO at pH 3.30–3.14, the grain size of CoO decreases from 33.47 to 8.85 nm by increasing the concentration of TEOS from 0 to 0.005 M. When 0.01 M TEOS is added to prepare the precursor of CoO, the irreversible discharge capacity at the first cycle can be completely recovered in the activation period with the activation rate of 16.50 mAh/g cycle, and the capacity fading fraction at 80th cycle is found to be 16.7%.
關聯:	Journal of the Taiwan Institute of Chemical Engineers
显示于类别:	[化工與材料工程系(所)] 【化工與材料工程系】期刊論文