Preparation and Characterisation of Polyethersulfone Filled with Silica Nanoparticles” Polym. Polym. Compos

NCUTIR > College of Engineering > Department of Chemical and Materials Engineering > 【化工與材料工程系】期刊論文 > Item 987654321/5839

Please use this identifier to cite or link to this item: http://ir.lib.ncut.edu.tw/handle/987654321/5839

Title:	Preparation and Characterisation of Polyethersulfone Filled with Silica Nanoparticles” Polym. Polym. Compos
Authors:	Chium, Cheng-Fang Ou and Shing-Jyun
Contributors:	圖書館
Date:	2015
Issue Date:	2016-10-14 11:44:41 (UTC+8)
Abstract:	This study was performed primarily to investigate the effects of chemical modification on silica surface and the silica content on the thermal and gas barrier properties of a polyethersulfone (PES) matrix. The PES/SiO2 composites composed of PES and three species of SiO2 nanoparticles (AEROSIL A200, R805 and R974) were prepared by solution blending. The thermal behaviour, thermal stability, and morphology of the composites were studied by DSC, TGA and SEM. The oxygen barrier efficiency of the composites was characterized by use of an oxygen transmission rate (OTR) analyzer. The composites’ properties, such as glass transition temperature (Tg ), decomposition temperature (Td ), and oxygen barrier, were found to improve. The Tg s of the composites increased significantly with the silica content and the 10 wt.% R805 composite exhibited the highest Tg, which was 28.7 °C higher than that of pure PES (193.8°C). The Td s of these composites increased from 4.9 °C to 10.6 °C with silica content ranging from 0.5~10 wt.%. The added SiO2 leads to an increase in Tg and Td .The oxygen barrier effectiveness of the composites showed significant improvement when compared to pure PES. The 1 wt.% R974 composite exhibited the lowest OTR, a decrease of 62% when compared to pure PES. These results indicate that the PES/SiO2 composites have high potential for flexible polymer substrate applications.
Relation:	Polymers & Polymer Composites
Appears in Collections:	[Department of Chemical and Materials Engineering] 【化工與材料工程系】期刊論文