Effect of PMMA and Graphene Addition on the Performances of Organic Solar Cells

勤益科大機構典藏 > 工程學院 > 化工與材料工程系(所) > 【化工與材料工程系】期刊論文 > Item 987654321/6002

請使用永久網址來引用或連結此文件: http://ir.lib.ncut.edu.tw/handle/987654321/6002

題名:	Effect of PMMA and Graphene Addition on the Performances of Organic Solar Cells
作者:	歐珍方
貢獻者:	化工與材料工程系
日期:	2013-08
上傳時間:	2017-09-26 13:18:57 (UTC+8)
摘要:	Poly(3-hexylthiophene) (P3HT) is a wide application in active layer of solar cell. It is a soluble conductive polymer but their mechanical properties are poor and its conductivity is unstable in environmental condition. We add polymethylmethacrylate (PMMA) into active layer to overcome these disadvantages. We investigated the effect of adding PMMA and graphene into solar cell on its characteristics of polymer solar cell. The cell structure was ITO/PEDOT:PSS/P3HT:PCBM:PMMA/Ca/Al. The 0.02, 0.04 and 0.06 weight ratio of PMMA were added into the P3HT:PCBM (1:1 ratio by weight) active layer. The device with 0.04 PMMA exhibits the highest short circuit current density (Jsc, 9.01 mA/cm2) and power conversion efficiency (PCE, 3.39%). The increases of Jsc and PCE are 26.5% and 49.3%, respectively compared with the device based on the pristine P3HT:PCBM active layer giving Jsc and PCE of 7.12 mA/cm2 and 2.27%. Graphene exhibits good electron conductivity, thermal conductivity, chemical stability and strength. We investigated the effect of inserting graphene between hole transfer layer (HTL) of poly(ethylene dioxythiophene) (PEDOT)-polystyrene sulfonic acid (PSS) (PEDOT:PSS) and active layer on the characteristics of polymer solar cell. The cell structure was ITO/PEDOT:PSS/Graphene/P3HT:PCBM:PMMA/Ca/Al. The concentration of graphene solution was 2.2 mg/ml and the graphene layer was coated by spin-coating at 6000 rpm and the weight ratio of PMMA in the P3HT:PCBM active layer was 0.04. The Jsc of device was increased to 9.45 mA/cm2, an increase of 32.7%. The PCE of the device was increased to 3.63%, an increase of 59.9%. © (2013) Trans Tech Publications, Switzerland. (9 refs)
關聯:	Advanced Materials Research
顯示於類別:	[化工與材料工程系(所)] 【化工與材料工程系】期刊論文

文件中的檔案:

沒有與此文件相關的檔案.

檢視Licence

在NCUTIR中所有的資料項目都受到原著作權保護.

資料載入中.....