题名:	The Properties of Nickel Hydroxide Electrode in Formation of Ni/MH Battery
作者:	杜景順
贡献者:	化工與材料工程系
日期:	2011-03
上传时间:	2017-11-14 10:41:38 (UTC+8)
摘要:	Nickel metal hydride (Ni/MH) batteries are presently as the promising high capacity power sources applied in the various portable electronic devices and the hybrid electric vehicles. After a Ni/MH battery was assembled, the forming process was carried out to assure its performances, which included the high charge/discharge capacity, the good cycle durability, and the low internal resistance. The effect of charging current, charging temperature, concentration of KOH, concentration of LiOH, soaking time, and soaking temperature on the formation of a Ni/MH battery was investigated in the present work. The experimental results indicate that the best utilization of the positive electrode is found to be 86.3% at the conditions of 0.2C charging current, 25 °C, 7.129 M KOH and 0.477 M LiOH for the battery soaked at 30 °C for 12 h. The electrochemical properties of Ni/MH battery are investigated by AC impedance, and the elements of equivalent circuit for various forming conditions are evaluated by using the complex nonlinear least square (CNLS) technique. The active material β-Ni(OH)2 in the positive electrode is transformed to β-NiOOH and γ-NiOOH in the forming process observed by the X-ray diffraction (XRD) analysis. When the soaking time and temperature of the forming process increase, the utilization of positive electrode increases due to the increase in its electroactive area and fraction of γ-NiOOH.
關聯:	Rare Metals
显示于类别:	[化工與材料工程系(所)] 【化工與材料工程系】期刊論文

文件中的档案:

没有与此文件相关的档案.

检视Licence

在NCUTIR中所有的数据项都受到原著作权保护.

数据加载中.....