勤益科大機構典藏:Item 987654321/1938
English  |  正體中文  |  简体中文  |  Items with full text/Total items : 2928/5721 (51%)
Visitors : 375467      Online Users : 186
RC Version 6.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
    •  Adv. Search
    Home ‧ Login ‧ Upload ‧ Help ‧ About ‧ Administer Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncut.edu.tw/handle/987654321/1938


    Title: 工程塑膠增韌環氧樹脂之破壞特性
    Authors: 施文昌
    Shih, Wen-Chang
    Contributors: 化學工程系
    Department of Chemical Engineering
    Keywords: 工程塑膠;環氧樹脂
    Date: 1993-12
    Issue Date: 2008-12-05 10:25:58 (UTC+8)
    Publisher: 勤益科技大學
    Abstract: 本文主要探討工程塑膠PC，Phenoxy及blocked PU增韌環氧樹脂之破壞機構當改變工程塑膠含量時，會呈現不同之裂縫圖形；且增韌的程度受基材與環氧樹脂的相容性，形成之粒子大小及基材的特性等所影響。從動態實驗中，我們發現在環氧樹脂中含有10phr的blocked PU或10phr的Phenoxy展現較佳的增韌效果，而PC增韌環氧樹脂則無顯著的變化。從靜態實驗中，我們也觀察到15phr的blocked PU或10phr的PC展現較佳的增韌結果，但Phenoxy增韌環氧樹脂則無顯著的影響，此外，我們也藉SEM照片觀察增韌機構中的破壞形態。
    The fracture properties of toughenes epoxy by Phenoxy, Polycarbonate and blocked NCO-terminated PU prepolymer were studied. The toughening mecha-nism of the system was investigated. Different crack patterns were observed on specimens of different plastic contents. The toughness of a toughened material is affected by the amount of particles, the miscibility of particle and matrix material, and the property of matrix material. Under dynamic condition, the epoxy resin containing 10 phr blocked NCO-terminated PU prepolymer or 10 phr Phenoxy showed good toughness. On the other hand, the effect of adding Polycarbonate on toughness of epoxy resin is insignificant. Under quasi-static condition, the best toughening result of resin by adding blocked NCO-terminated PU prepolymer and Polycarbonate was obtained at 15 phr and 10 phr separately, and the toughening effect is insignificant by adding Phenoxy in epoxy. The toughening mechanism was investigated by examining the fracture morphology with SEM photographs.
    Relation: 勤益學報 No.11 p.83-91
    Appears in Collections:[National CHIN-YI University of Technology] 勤益學報

    Files in This Item:

    File Description SizeFormat
    工程塑膠增韌環氧樹脂之破壞特性.pdf1106KbAdobe PDF2683View/Open


    All items in NCUTIR are protected by copyright, with all rights reserved.

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback